초록

When the cotton/polyester fiber mixed fabrics were treated with ferrous sulfate and oxalic acid for burn out finishing, it was examined how the effects of process conditions as concentration of burn out agents, temperature, time and pressure act onto the properties of polyester ground fabrics. The results are as follows. The effect of burn out finishing by pressure was greated in 3kgf/cm2. The properties as white index and tensile strength of polyester ground fabrics were decreased according as processing concentration, temperature time increases. The shrinkage was increased according as processing concentration, temperature time increases. The optimum condition of burn out agents to ferrous sulfate was 30% concentration, 150oC, 1min, 3kgf/cm2 and to oxalic acid was 10% concentration, 110oC, 1min, 3kgf/cm2. And the optimum of ferrous sulfate and oxalic acid used in combination was 10% ferrous sulfate and 7% oxalic acid, 110oC, 1min., 3kgf/cm2.